A cylindrical copper single crystal, oriented along the $[123]-$direction, is deformed in tension.

a$)$ What shape change do you expect $($Hint: in fcc crystals deformation takes place on $\{111\}-$

planes$)?$

b$)$ What change would you expect, if the single crystal is replaced by a polycrystal?