the answer is there i just want it to be written clearly

Question # 3: Briefly explain why, for small anode-to-cathode area ratio, the corrosion rate will be higher than for a large ratio. for a small anode to cathode area into the conosion rone will be higher than for large ratio because from this equation ran the rate of corrosion is directly proportional to the current density. Hence, toy some giren curent fic associated with the corrosion reachon, for a small area ratio the cumont Jenshy at the anode will be greater than for a longe ratio - Because alea cf cathode will be loroge so the electrons that aw produced from the anodicarea are consumed at ci faster rate, therfore Corrosion rate win be higher opposite is true when anodic area is larger than Catholic ana